LEXAN™
FL930 resin
聚碳酸酯
30%
玻璃纤维增强材料
SABIC Innovative Plastics Asia Pacific
产品说明:
Various weight reductions at 0.250" (6.35 mm) wall, 30% GR. Superior
flex strength/modulus, good tensile strength. V-0/5VA at 0.250" (6.35
mm).
| 总体 | ||||
|
材料状态
|
|
|||
|
资料 1
|
|
|||
|
UL 黄卡 2
|
|
|||
|
搜索 UL
黄卡
|
|
|||
|
供货地区
|
|
|||
|
填料/增强材料
|
|
|||
|
特性
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
ASTM D792 | ||
|
-- 3
|
1.29
|
g/cm³
|
|
|
--
|
1.43
|
g/cm³
|
|
|
收缩率 - 流动 (6.40 mm)
|
0.20 到 0.40
|
%
|
内部方法 |
|
吸水率
|
ASTM D570 | ||
|
24
hr
|
0.12
|
%
|
|
|
平衡,
23°C
|
0.26
|
%
|
|
|
Foam - Physical 4
|
10
|
%
|
内部方法 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量 (6.40 mm)
|
6930
|
MPa
|
ASTM D638 |
|
抗张强度 (屈服, 6.35
mm)
|
72.4
|
MPa
|
ASTM D638 |
|
伸长率 (断裂, 6.35
mm)
|
3.0
|
%
|
ASTM D638 |
|
弯曲模量 (6.40 mm)
|
6890
|
MPa
|
ASTM D790 |
|
弯曲强度 (屈服, 6.40
mm)
|
128
|
MPa
|
ASTM D790 |
|
Foam - Mechanical 4
|
10
|
%
|
内部方法 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
无缺口悬臂梁冲击 (23°C)
|
480
|
J/m
|
ASTM D4812 |
|
落锤冲击 (23°C)
|
40.7
|
J
|
内部方法 |
|
Foam - Impact 4
|
10
|
%
|
内部方法 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
ASTM D648 | ||
|
0.45 MPa,
未退火, 6.40 mm
|
143
|
°C
|
|
|
1.8 MPa,
未退火, 6.40 mm
|
139
|
°C
|
|
|
线形热膨胀系数 - 流动 (-40 到 95°C)
|
2.2E-5
|
cm/cm/°C
|
ASTM E831 |
|
比热
|
1050
|
J/kg/°C
|
ASTM C351 |
|
导热系数
|
0.16
|
W/m/K
|
ASTM C177 |
|
RTI Elec
|
110
|
°C
|
UL 746 |
|
RTI Imp
|
110
|
°C
|
UL 746 |
|
RTI
|
110
|
°C
|
UL 746 |
|
Foam - Thermal 4
|
10
|
%
|
内部方法 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
> 1.1E+17
|
ohm
|
ASTM D257 |
|
体积电阻率
|
2.4E+17
|
ohm·cm
|
ASTM D257 |
|
介电常数
|
ASTM D150 | ||
|
100
Hz
|
2.70
|
|
|
|
1
MHz
|
2.61
|
|
|
|
耗散因数
|
ASTM D150 | ||
|
100
Hz
|
3.4E-3
|
|
|
|
1
MHz
|
7.5E-3
|
|
|
|
耐电弧性 5
|
PLC 7
|
|
ASTM D495 |
|
相比耐漏电起痕指数(CTI)
|
PLC 4
|
|
UL 746 |
|
高电弧燃烧指数(HAI)
|
PLC 4
|
|
UL 746 |
|
高电压电弧起痕速率 (HVTR)
|
PLC 3
|
|
UL 746 |
|
热丝引燃 (HWI)
|
PLC 1
|
|
UL 746 |
|
Foam - Electrical 4
|
20
|
%
|
内部方法 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级 (5.99 mm)
|
|
|
UL 94 |
|
极限氧指数
|
40
|
%
|
ASTM D2863 |
|
Foam - Flame Class Minimum
Density
|
900
|
kg/m³
|
内部方法 |
| 补充信息 | |||
|
Structural Foam Molding - Blowing Agent,
Chemical System: FLC95
Structural Foam Molding - Blowing Agent, Physical System: Nitrogen Structural Foam Molding - Concentration Range (Blowing Agent): 3 - 5 % Structural Foam Molding - Drying Temperature (Blowing Agent): 104 °C Structural Foam Molding - Drying Temperature (Resin): 121 °C Structural Foam Molding - Drying Time (Blowing Agent): 4 hrs Structural Foam Molding - Drying Time (Resin): 3 - 4 hrs Structural Foam Molding - Drying Time (Resin, Cumulative): 48 hrs Structural Foam Molding - Front Temperature: 293 - 310 °C Structural Foam Molding - Melt Temperature: 288 - 316 °C Structural Foam Molding - Middle Temperature: 293 - 310 °C Structural Foam Molding - Mold Temperature: 71 - 93 °C Structural Foam Molding - Nozzle Temperature: 271 - 293 °C Structural Foam Molding - Rear Temperature: 254 - 266 °C Structural Foam Molding - Recommended Concentration (Blowing Agent): 1.5 % |
| 备注 |
| 1通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。 |
| 2UL 黄卡含有 UL 验证的易燃性和电气特性。 |
| 3Foam molded |
| 46.4 mm wt reduction |
| 5钨电极 |